High silica fiberglass filtration mesh for steel

  • High silica fiberglass filtration mesh for steel


    Application: Filtration of molten steel, Iron, copper and aluminium.


    It is weaved by high silica fiberglass yarn and coated with special refractory coating. It can effectively remove slag, refractory particles and non-metallic inclusions from molten metals. Made from specially treated silica yarns, the thick type silica mesh filters are capable of withstanding pouring temperature up to 1620℃.

    Silica mesh filter are ideal for in-mold filtration of gray, malleable, white, compacted graphite and ductile cast irons, as well as non-ferrous aluminum and copper-based metal alloys and many types of small scale steel casting filtration.

    Besides the function of molten metal filters, it could be also used for riser knock-off or de-gating knock-off. Investment casters have also placed the perform cup shape filters in the wax mold gating systerm to filter metal at pattern entry.


    Type

    Fiberglass filtration mesh for steel

    Work Temperature

    1620

    Softening Temperature

    1700

    Continuous Working Hours

    10 Min.1400-1450℃)

    4 Min.1450-1560℃)

    15 Seconds.1560-1620℃)

    Gas Emit

    60cm 3/g

    Thickness

    1.5mm

    Weight

    520-580 g/m2

    Hole Size

    1.5*1.5/2.0*2.0/2.5*2.5mm

    Weave Pattern

    Mock Leno